Author
Sakakibara, Akira
Kanadani, Teruto
Abstract
Aging of diolute Al-Ag alloys after quenching from low temperatures were studied mainly by electrical resistometry. Maximum resistivity observed in the aging curve of specimens quenched from high temeperature disappeared when the quenching temperature was lowered to 473 or 453K. When the quenching temperature was lowered further to 423K or lower, however, maximum resistivity reappeared. At the temperature lower than or equal to 423K but higher than the GP zone solvus, the alloys were not homogeneous but had clusters of solute atoms or fluctuation of solute concentration. Inhomogeneous distribution of solute atoms may affect the aging behavior after quenching from that temperature.
Publication Title
Memoirs of the Faculty of Engineering, Okayama University
Published Date
1998-11-30
Volume
volume33
Issue
issue1
Publisher
Faculty of Engineering, Okayama University
Publisher Alternative
岡山大学工学部
Start Page
1
End Page
4
ISSN
0475-0071
NCID
AA10699856
Content Type
Departmental Bulletin Paper
OAI-PMH Set
岡山大学
language
English
File Version
publisher
NAID
Eprints Journal Name
mfe