Abstract | A new material of higher fullerene, RbxC84, was synthesized by intercalating Rb metal into C-84 crystals. The RbxC(84) crystals showed a simple cubic (sc) structure with lattice constant, a, of 16.82 (2) angstrom at 6.5 K, and 16.87 (2) angstrom at 295 K. The Rietveld refinements were achieved with the space group, Pa (3) over bar, based on a model that the C-2 axis of D2d-C84 aligned along [111]. The sample composition was determined to be Rb-8.8(7) C-84. The ESR spectrum at 303 K was composed of a broad peak with peak-to-peak linewidth Delta H-pp of 220 G, and a narrow peak with Delta H-pp of 24 G. Temperature dependence of the broad peak clearly showed a metallic behavior. The metallic behavior was discussed based on a theoretical calculation. This finding of new metallic phase in a higher fullerene is the first step for a development of new types of fullerene materials with novel physical properties such as superconductivity. |
Note | Published with permission from the copyright holder.
This is the institute's copy, as published in Physical Review B, June 2005, Volume 71, Issue 22, Pages 6. Publisher URL: href="http://dx.doi.org/10.1103/PhysRevB.71.224118 Direct access to Thomson Web of Science record Copyright © 2005 The American Physical Society. All rights reserved. |
Published Date | 2005-6
|
Publication Title |
Physical Review B
|
Volume | volume71
|
Issue | issue22
|
Content Type |
Journal Article
|
language |
English
|
Refereed |
True
|
DOI | |
Web of Science KeyUT | |
Submission Path | physics_general/34
|