| Abstract | Aging behavior of Al-0.23mass % Si alloy was studied by measurements of elecrical resistivity. Resistvity maximum was observed in the aging curves at 273K after quenching from various temperatures. Appearance of maximum and its dependence on the quenching temperature were attributed to the formation of GP zones. Even in a more dilute alloy as 0.01mass % Si, the maximum of resistivity was also recognized.
|
| Publication Title |
Memoirs of the Faculty of Engineering, Okayama University
|
| Published Date | 1990-03-29
|
| Volume | volume24
|
| Issue | issue2
|
| Publisher | Faculty of Engineering, Okayama University
|
| Publisher Alternative | 岡山大学工学部
|
| Start Page | 11
|
| End Page | 16
|
| ISSN | 0475-0071
|
| NCID | AA10699856
|
| Content Type |
Departmental Bulletin Paper
|
| OAI-PMH Set |
岡山大学
|
| language |
English
|
| File Version | publisher
|
| NAID | |
| Eprints Journal Name | mfe
|