三浦 嘉也
Department of Applied Chemistry
河村 利夫
Department of Applied Chemistry
|
抄録 | Zinc oxide films were prepared on silica glass substrates by the use of an r.f. activated reactive evaporation (ARE) method, and were examined by X-ray diffraction (XRD) and scanning electron micrograph (SEM). XRD measurements indicate that the films were c-axis oriented and that an r.f. plasma of Zn and O was necessary for the ZnO film deposition. Substrate temperature, oxygen gas pressure, evaporation rate, r.f. power and inlet position of oxygen gas effect the c-axis orientation, the growth rate and the microstructure of the films. Optimum conditions for a dense film with a fine texture of the surface and having good crystallinity were as follows: the substrate temperature;400℃, the evaporation rate;5.0(A)/s, the oxygen pressure;2.0x10(-4) Torr, the r.f. power;150 to 200W, and the oxygen gas inlet near the substrate. For the film prepared under the optimum conditions, the standard deviation σ of the rocking curve for the (002) diffraction was 1.9deg, smaller than that of the film prepared by using an r.f. sputtering method.
|
出版物タイトル |
Memoirs of the Faculty of Engineering, Okayama University
|
発行日 | 1990-12-14
|
巻 | 25巻
|
号 | 1号
|
出版者 | Faculty of Engineering, Okayama University
|
出版者(別表記) | 岡山大学工学部
|
開始ページ | 23
|
終了ページ | 35
|
ISSN | 0475-0071
|
NCID | AA10699856
|
資料タイプ |
紀要論文
|
OAI-PMH Set |
岡山大学
|
言語 |
英語
|
論文のバージョン | publisher
|
NAID | |
Eprints Journal Name | mfe
|