The state above the solubility temperature of GP zones of Al-3mass % Mg alloy, which has a tendency for precipitation and preprecipitation at low temperature, was studied by resistivity measurement. Homogenization treatment at high temperature reduced Mg atoms in the surface layer. After quenching from 623K, the specimen was annealed sequentially at various temperatures above the GP zone solvus. The stationary resistivity obtained in annealing at a temperature was the same irrespective of the starting state and increased with decreasing annealing temperature. No precipitation was observed in the annealing. The results are not in favor of the segregation of Mg atoms to the dislocation loops but of the short range clustering.
出版物タイトル
Memoirs of the Faculty of Engineering, Okayama University
発行日
1994-03-15
28巻
2号
出版者
Faculty of Engineering, Okayama University
出版者(別表記)
岡山大学工学部
開始ページ
9
終了ページ
12
ISSN
0475-0071
NCID
AA10699856
資料タイプ
紀要論文
OAI-PMH Set
岡山大学
言語
English
論文のバージョン
publisher
NAID
Eprints Journal Name
mfe