榊原 精 Department of Mechanical engineering
Kanadani, Teruto Okayama University of Science
抄録
Fatigue strength of Al-Cu alloy was examined by a repeated tensile mode when the specimens were aged and reversion annealed. The specimen quenched from 723K and aged fully around room temperature showed fatigue strength which depended on the existence of soft layer, while the specimen quenched from 723K and aged in the same way showed fatigue strength independent of the existence of the soft layer. Fatigue strength of the specimen, of which the soft surface layer was removed, was the same for either quenching temperature. Fatigue strength became higher when the soft surface layer was thickened with reversion annealing for 600s at 323K after aging. The soft surface layer was thought to increase fatigue strength of the aged Al-Cu alloy as well as Al-Zn alloy.
出版物タイトル
Memoirs of the Faculty of Engineering, Okayama University
発行日
1996-03-29
30巻
2号
出版者
Faculty of Engineering, Okayama University
出版者(別表記)
岡山大学工学部
開始ページ
9
終了ページ
13
ISSN
0475-0071
NCID
AA10699856
資料タイプ
紀要論文
OAI-PMH Set
岡山大学
言語
English
論文のバージョン
publisher
NAID
Eprints Journal Name
mfe