著者 Shimizu, Kenichi| Torii, Tashiyuki| Ishida, Koki|
抄録 Using a fatigue testing method by which fatigue cracks can be initiated and propagated in a film adhered to cover an elliptical through-hole in a base plate subjected to push-pull cyclic loads, annealed copper films with the thickness of 100μm and those reduced the thickness from the 100μm to 50μm by an electro-polishing were fatigued under a constant stress amplitude with a stress ratio of zero. The crystal rotation behavior with the fatigue crack propagation was investigated by measuring the crystal orientation around the fatigue crack initiated from the notch root before and after fatigue testing, using EBSD (Electron Back-scatter Diffraction) method. Then, the change of crystal orientation with fatigue testing was evaluated quantitatively from the misorientation between the crystal orientation matrix on the same point obtained before and after fatigue testing. As a result, the angle of the crystal rotation obtained from the region showing the high fatigue crack propagation rate was larger than that obtained from the region showing the low fatigue crack propagation rate for the film with the thickness of 100μm, while the fatigue crack propagated faster in the film with the thickness of 50μm than that with the thickness of 100μm regardless of the small crystal rotation angles with the fatigue testing for the film with the thickness of 50μm.
出版物タイトル Memoirs of the Faculty of Engineering, Okayama University
発行日 2009-01
43巻
開始ページ 1
終了ページ 7
ISSN 1349-6115
言語 英語
論文のバージョン publisher
NAID 120002308710
JaLCDOI 10.18926/14096
フルテキストURL Mem_Fac_Eng_OU_40_1_1.pdf
著者 馬 有理| 清水 憲一| 鳥居 太始之|
抄録 A testing for bent fatigue crack propagation under mixed-mode conditions was carried out using fatigue and annealed slant precracks with different slant angles, β ,defined as the angle between loading and precrack directions in a rectangular plate. As a result, bent fatigue crack from the fatigue precrack with β =45deg. propagated under mixed-mode conditions with mode II stress intensity factor (K(II))(est) evaluated from the discontinuous displacement measured along the crack. On the other hand, bent fatigue crack from the fatigue precrack with β =60deg. and from the annealed precracks with both slant angles of β =60deg. and β =45deg. propagated under the mode I behavior. This was because the compressive residual stress near the fatigue precrack caused contact to each other between the upper and the lower surfaces of the precrack with the smaller slant angle β . Furthermore, the fatigue crack propagation rates indicated almost the same relationship for all the data, using the mixed-mode effective stress intensity factor (K(M))(est), calculated from the discontinuous displacement measured along the bent fatigue crack.
出版物タイトル Memoirs of the Faculty of Engineering, Okayama University
発行日 2006-01
40巻
1号
開始ページ 1
終了ページ 8
ISSN 0475-0071
言語 英語
論文のバージョン publisher
NAID 120002308402
JaLCDOI 10.18926/14069
フルテキストURL Mem_Fac_Eng_OU_42_104.pdf
著者 Donghui, MA| Torii, Tashiyuki| Shimizu, Kenichi| Matsuba, Akira|
抄録 As model specimens of surface film-bonded materials, pure copper films with a thickness of 100μm were bonded to the surface of steel base with epoxy resin, where the tensile residual stress was measured by an X-ray on the surface copper film. The distribution of initial electric resistance was measured on both copper film and base specimen by a direct current potential drop technique. As a result, there was a good agreement between the measured and theoretical values. From the fatigue testing results, it was shown that the measured electric resistance increased with the fatigue crack length on the copper film, which was almost equal to the theoretical value calculated for a central slit in a plate with finite width. This was probably because the fatigue crack was opened due to the tensile residual stress on the film even under unloading condition. In addition, the internal crack length during fatigue was examined by ultrasonic testing for the film-bonded specimen. As a result, there was a difference in the fatigue crack length between the surface copper film and the inner base.
出版物タイトル Memoirs of the Faculty of Engineering, Okayama University
発行日 2008-01
42巻
1号
開始ページ 104
終了ページ 109
ISSN 0475-0071
言語 英語
論文のバージョン publisher
NAID 120002308537