Fine particles of Ti-V alloy were prepared by means of arc method and were investigated on internal structure and phase transformation using HR-TEM and EDS. Martensite phase was observed in a particle containing comparatively low concentration of V, and ω phase was also found to exist in a nearly 15% V particle. The structure of the ω phase in the fine particle is remarkably expanded in comparison with the bulk sample, and the ω phase is unstable, so that it has disappeared in a few seconds during TEM observation.
Publication Title
Memoirs of the Faculty of Engineering, Okayama University
Published Date
1997-03-28
Volume
volume31
Issue
issue2
Publisher
Faculty of Engineering, Okayama University
Publisher Alternative
岡山大学工学部
Start Page
11
End Page
20
ISSN
0475-0071
NCID
AA10699856
Content Type
Departmental Bulletin Paper
OAI-PMH Set
岡山大学
language
English
File Version
publisher
NAID
Eprints Journal Name
mfe