Sakakibara, Akira
Kanadani, Teruto
Abstract
Effect of addition of Fe on the occurrence of serration in Al-12mass%Zn alloys was investigated. Specimens aged at 293K for various periods after quenching from various temperatures (T(Q)), 398K to 823K, were tensile-tested at room temperature. Serration occurred more easily and more remarkably with decreasing T(Q) for as-quenched specimens: in the case that T(Q)=448K serration was observed both for the binary and Fe added alloys, while in the case that T(Q)=573K none of the three alloys showed serration. For the binary alloy serration was observed only when the aging period was short enough, but addition of Fe to the binary alloy prolonged the aging period where serration could be recognized. Aging rate measured by hardness was remarkably retarded with the increase of Fe addition. These results confirm the interpretation that the serration in Al-Zn alloy occurs in the early stage of aging where small GP zones or solute clusters are formed.
Publication Title
Memoirs of the Faculty of Engineering, Okayama University
Published Date
2003-03
Volume
volume37
Issue
issue2
Publisher
Faculty of Engineering, Okayama University
Start Page
1
End Page
4
ISSN
0475-0071
NCID
AA10699856
Content Type
Departmental Bulletin Paper
OAI-PMH Set
岡山大学
language
English
File Version
publisher
NAID
Eprints Journal Name
mfe