Fine particles of Ti-V alloy were prepared by means of arc method and were investigated on internal structure and phase transformation using HR-TEM and EDS. Martensite phase was observed in a particle containing comparatively low concentration of V, and ω phase was also found to exist in a nearly 15% V particle. The structure of the ω phase in the fine particle is remarkably expanded in comparison with the bulk sample, and the ω phase is unstable, so that it has disappeared in a few seconds during TEM observation.
Published Date
1997-03-28
Publication Title
Memoirs of the Faculty of Engineering, Okayama University
Publication Title Alternative
岡山大学工学部
Volume
volume31
Issue
issue2
Publisher
Faculty of Engineering, Okayama University
Publisher Alternative
岡山大学工学部
Start Page
11
End Page
20
ISSN
0475-0071
NCID
AA10699856
Content Type
Departmental Bulletin Paper
language
英語
File Version
publisher
Refereed
False
Eprints Journal Name
mfe