Sakakibara, Akira
Hida, Moritaka
Abstract
Fine particles of Ti-Mo alloy have been prepared by means of arc method, and investigated on internal structure and phase transformation using HR-TEM and EDS. Martensite phase was observed in a particle containing comparatively low concentration of Mo, and ω phase was also found to exist in a nearly 14 % M0 particle. The structure of the ω phase in the fine particle is expanded and remarkably unstable in comparison with the bulk sample, so that it has disappeared in a few seconds during TEM observation. Moreover, the β structure of Ti-Mo particles has changed to the unusual fcc phase with irradiation of a strong electron beam.
Publication Title
Memoirs of the Faculty of Engineering, Okayama University
Published Date
1994-03-15
Volume
volume28
Issue
issue2
Publisher
Faculty of Engineering, Okayama University
Publisher Alternative
岡山大学工学部
Start Page
1
End Page
7
ISSN
0475-0071
NCID
AA10699856
Content Type
Departmental Bulletin Paper
OAI-PMH Set
岡山大学
language
英語
File Version
publisher
NAID
Eprints Journal Name
mfe