FullText URL | AEZ54_4_389.pdf Fig.pdf |
---|---|
Author | Sakakibara, Akira| Takebe, So| Ide, Toru| Hayakawa, Tohru| |
Keywords | Bacillus thuringiensis Cry46Ab toxin Planar lipid bilayer Single-channel analysis Calcein release assay |
Published Date | 2019-08-16 |
Publication Title | Applied Entomology and Zoology |
Volume | volume54 |
Issue | issue4 |
Publisher | Springer |
Start Page | 389 |
End Page | 398 |
ISSN | 0003-6862 |
NCID | AA00543238 |
Content Type | Journal Article |
language | English |
OAI-PMH Set | 岡山大学 |
File Version | author |
DOI | 10.1007/s13355-019-00635-z |
Web of Science KeyUT | 000503219100007 |
Related Url | isVersionOf https://doi.org/10.1007/s13355-019-00635-z |
JaLCDOI | 10.18926/46946 |
---|---|
FullText URL | mfe_38_1-2_001_004.pdf |
Author | Sakakibara, Akira| Kanadani, Teruto| |
Abstract | The relationship between occurrence of serration and reversion heat treatment was studied by tensile test on Al-10mass%Zn alloy. Serration was observed for the furnace cooled specimen, but not for the as-quenched one and the shortly aged one, which result is difficult to be interpreted by the Cottrell theory. The stress amplitude in the serration increased with increasing the time of annealing for reversion up to 10ks and then stayed at a constant value which might be interpreted by the Cottrell theory. The stress amplitude in the serration decreased with increasing the annealing temperature, which is contrary to the prediction by the Cottrell theory. The specimen directly annealed without aging and the one annealed after aging agreed well with each other in the tensile strength and the stress amplitude in the serration, which suggests solute clusters as the cause of serration. |
Publication Title | Memoirs of the Faculty of Engineering, Okayama University |
Published Date | 2004-03 |
Volume | volume38 |
Issue | issue1-2 |
Start Page | 1 |
End Page | 4 |
ISSN | 0475-0071 |
language | English |
File Version | publisher |
NAID | 80016785932 |